Simulation of environmentally assisted failure of metals (DLR.6193)

Project nummer: dlr6193

Omschrijving van het onderzoek

The combined influence of stress and an aggressive environment leads to a form of localised damage that is commonly known as Stress Corrosion Cracking (SCC). Electrochemical actions tend to intensify the crack growth and to decrease the resistance to final fracture. This form of corrosion attack has led to catastrophic failures in structural and aircraft systems. In this research a significant advance will be realised by combining available models with computational failure mechanics methods, including the analysis of stochastic variability of the involved variables. The research will provide a rational means for risk analysis based on a fundamental model applicable to a broad spectrum of situations.

Gebruikers

Er zijn zeven bedrijven bij dit project betrokken.

Projectleider

Dr. M.A. Gutiérrez

Technische Universiteit Delft
Lucht- en Ruimtevaarttechniek
Technische Mechanica

Postbus 5058
2600 GB Delft

Status van het project

Gestart	: 01-01-2004
Einddatum	: 01-01-2009

Trefwoorden

Corrosie, Damage, Finite elements, Localisatie, Lucht- en ruimtevaarttechniek, Mechanics, Reliability, Stress corrosion cracking

Print | Over deze site |

Sitemap | Voorbehoud | Gewijzigd 17-5-2006

Nieuws uitgelicht

Nieuwsbrief Technologiestichting STW, januari 2012

31 januari 2012

Elke maand stuurt Technologiestichting STW haar relaties een link naar de web-based nieuwsbrief. Hierin staat een maandelijks overzicht van het jongste nieuws van de bestuurstafel, onderzoeksnieuws, o... [meer]